RICOCEL ES-3261R is a high heat resistant glass fiber epoxy resin laminated board for solder pallet.
Component mounting by automatic soldering machine is performed through two kind of work processes.
Generally, it is performed in the order of reflow soldering to wave soldering.
At the wave soldering process, it is necessary to apply solder only to soldering part, with the components mounted by reflow soldering being protected.
RICOCEL is the tool used in the process of wave soldering.
RICOCEL has pockets to protect the pre-mounted components and has through-holes to apply solder only to soldering spots.
Features
- Defective soldering caused by solder pallet warpage can be reduced with ES-3261R’s excellent low warpage property.
- Durable for fine design with excellent mechanical strength, dimensional stability and heat resistance.
- Parts on PWBs can be protected against static damage with ES-3261R’s excellent static dissipation property.
- Excellent in chemical resistance such as Water-soluble flux and Alcohol-base flux.
- Compared to aluminum boards, fabrication cost of pallets can be reduced with less wear or less breakage of cutting tools.
- Compared to aluminum pallets, electricity expense can be reduced with ES-3261R’s excellent heat storage property.
Advantages of using solder pallet
Yield : Reduction of defective soldering
Masking process : Setting on pallet
Line width adjustment : Standardized
Thermal stress to electronic components : Small
Advantages
- 1. EXCELLENT DURABILITY
- Excellent durability against repetitive soldering of more than 20000-time.
- 2. EXCELLENT CHEMICAL RESISTANCE
- Excellent chemical resistance against soluble flux or pallet cleaner.
- 3. EXCELLENT MECHANICAL STRENGTH
- Excellent mechanical strength for fine machining.
Size of Blank Material
- Thickness : 1.6～6mm
- Length X Width : 1000X1200 mm 1200X2000 mm
Properties of RICOCEL ES-3261R
| Test items | Units | ES-3261R | |
|---|---|---|---|
| Reinforce material | Glass woven fabric | ||
| Surface resistance | 10 volts applied | Ω/□ | 105～109 |
| Glass transition temperature | DMA | degrees Celsius | 200 |
| TMA | 170 | ||
| Coefficient of thermal expansion | Zα1（50→100degrees Celsius） | ppm/℃ | 45 |
| Zα2（200→250degrees Celsius） | 200 | ||
| Warp/Fill（50→250degrees Celsius | 10/13 | ||
| Thermal conductivity | Probe | W/mK | 0.36 |
| Water absorption | ％ | 0.04 | |
Swipe horizontally to see the list.
The above figures are not guaranteed value but one of the test results at our laboratory.
Delivery Form of RICOCEL ES-3261R
Please choose from among the following three types of the delivery form of RICOCEL ES-3261R.
- Finished Product
- Finished product after machining such as cutting, grinding and drilling based on your drawing will be supplied.
- Board Cut to Specified Dimensions
- Board without machining such as drilling, etc. and in the form of simply cutting the material according to the specified dimensions will be supplied.
- Blank Material
- Blank material without any machining will be supplied.
Minimum Order Quantity
1 Piece.